BATEIG STONE
A biocalcerinite extracted in the province of Alicante (Spain). The extraction of Bateig Beige, Diamante, Galaxy, Fantasia, Azul and Maroc Claro is conducted on an uninterrupted basis in our own quarry.
HOMOGENEITY
This stone features a high degree of homogeneity due to the fact both its mechanical properties and appearance colour remain unchanged over time.
QUALITY
Its petrology and physical characteristics have gained the seal of quality awarded by the Laboratory of Applied Petrology of the University of Alicante.

SAMPLE COLLECTION
BATEIG BEIGE VERONA

Petrographic denomination: Biocalcerinite
Apparent density (kg / m³): 2170
Tensile strength under a concentrated load (Mpa): 8
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 6,4
Water absorption at atmospheric pressure (%): 6,9
BATEIG AZUL

Petrographic denomination: Biocalcerinite
Apparent density (kg / m³): 2260
Tensile strength under a concentrated load (Mpa): 12,2
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 11,5
Water absorption at atmospheric pressure (%): 5,6
BATEIG FANTASÍA

Petrographic denomination: Biocalcerinite
Apparent density (kg / m³): 2230
Tensile strength under a concentrated load (Mpa): 10,8
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 8,5
Water absorption at atmospheric pressure (%): 5,7
BATEIG GALAXY

Petrographic denomination: Biocalcerinite
Apparent density (kg / m³): 2260
Tensile strength under a concentrated load (Mpa): 12,2
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 11,5
Water absorption at atmospheric pressure (%): 5,6
BATEIG DIAMANTE

Petrographic denomination: Calcarenita
Apparent density (kg / m³): 2150
Tensile strength under a concentrated load (Mpa): 9,5
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 6,3
Water absorption at atmospheric pressure (%): 6,8
MAROC

Petrographic denomination: Calcirudite
Apparent density (kg / m³): 2230
Tensile strength under a concentrated load (Mpa): 7,0
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 5,5
Water absorption at atmospheric pressure (%): 3,8
BATEIG BEIGE GÉNOVA

Petrographic denomination: Biocalcerinite
Apparent density (kg / m³): 2170
Tensile strength under a concentrated load (Mpa): 8
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 6,4
Water absorption at atmospheric pressure (%): 6,9
BATEIG MESSIER

Petrographic denomination: Biocalcerinite
Apparent density (kg / m³): 2260
Tensile strength under a concentrated load (Mpa): 12,2
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 11,5
Water absorption at atmospheric pressure (%): 5,6
BATEIG UNIVERSO

Petrographic denomination: Calcarenita
Apparent density (kg / m³): 2150
Tensile strength under a concentrated load (Mpa): 9,5
Tensile strength under a concentrated load after freeze-thaw cycles (Mpa): 6,3
Water absorption at atmospheric pressure (%): 6,8